CITOCHROMAX N is a basic coated MMA electrode, for surfacing and joining ferritic to austenitic steels, dissimilar joining and difficult-to-weld steels. Also suitable for buffer layers when hardfacing. Stainless, fully austenitic chromium-nickel-manganese weld metal, small amounts of delta-ferrite are possible. The weld metal is highly crack-resistant and non-scaling up to +850 °C. The hardness of all-weld metal is ~180 HB, which work-hardens to ~450 HB under impact load. Highest operating temperature for dissimilar steel joints is +300 °C. In case of higher temperatures, use SUPRANEL 600 electrodes.

Tabs

Specification

Classification
EN 1470:	E Fe 10
EN 1600:	E 18 8 Mn B 2 2
AWS A5.4:	~E 307-15

Chemical analysis (Typical values in %)

C	Mn	Si	P	S	Cr	Ni
0.09	6	0.40	<0.025	<0.020	18.5	9

All-weld metal Mechanical Properties

Heat Treatment	Yield Strength N/mm2	Tensile strength N/mm2	Elongation A5 (%)	Impact Energy ISO - V (J)		Hardness
As Welded	> 350	>600	> 30	> 80 (+20 °C)	> 60 (-60 °C)	-

Materials

Dissimilar steels (Ferritic to Austenitic steels)
Joining difficult-to-weld steels; Manganese steels X120Mn12 (1.3401); Armor plates

Storage and redrying

Keep dry and avoid condensation.
Re-drying not generally required.
If necessary: 300-350 °C for 2 hours, 5 times max.