Magmaweld EH-360B - thick basic-covered electrode for depositing tough and wear resisting overlays on structural members subjected to severe wear. It is particularly resistant to high meta-to-metal wear, moderate impact and abrasion. The weld metal has sufficient red hardness up to +600°C. It can be machined only by grinding. Suitable hardfacing applications where wear resistance at higher temperatures is a prime concern, as in hot cut offs, dies for pressure castings, rolls, crushers excavator parts, bucket edges and bucket teeth, drilling bits, coal planes, conveyor screws. Multi-layers deposits will be free of cracks, even without depositing intermediate buffer layers. Only in case of very crack sensitive base metals, a tough buffer layer, made with ESB 40 or EI 307B electrodes, is required. Preferred to use with DC, electrode in positive (+) pole and also possible to use with AC.

Tabs

Спецификация

Classification
EN 14700	E Fe8
DIN 8555:	E 6-UM-60 (65W) T

Typical Chemical Analysis of All-Weld Metal (%)

C	Si	Mn	Cr	V	Fe
0.40	0.50	0.30	7.00	0.50	Rest

Typical Mechanical Properties of All-Weld Metal

Heat Treatment	Hardness (HRC)
As Welded	59

Storage and redrying information

It has to be dried at 350°C for 2 hours.
It should be stored in a dry room (relative humidity < 50%, room temperature > 20°C) on wooden pallets
It can be dried maximum 5 times.